IN THE NAME OF GOD

PHAROSIRAN®

 

 

Clinker & Portland Cement 

 

WHAT WE CAN SUPPLY?

 

  1. White Clinker type I

  2. Gray Clinker type I,II and V

  3. White Portland Cement type I

  4. Gray Portland Cement type I,II and V

    5.  

    "PACKING"

     

  5. Bulk without big bags

  6. 50 kg PP laminated bags

  7. Bulk in 1.5 M/T big bags

  8. 50 kg PP laminated bags in 1.5 M/T big bags

  9. 50 kg PP laminated bags on 1.5 M/T shrinked wooden pallet.

    10.  

    LOADING RATE PWWD

    IN

    BANDAR ABBASS & BIK PORTS

    IRAN

     

  10. 5,000.00 M/T for Bulk without big bags

  11. 1,500.00 M/T for 50 kg PP laminated bags

  12. 3,000.00 M/T for Bulk in 1.5 M/T big bags

  13. 3,000.00 M/T for 50 kg PP laminated bags in 1.5 M/T big bags

  14. 2,500.00 M/T for 50 kg PP laminated bags on 1.5 M/T shrinked wooden pallet.

    15.  

    "PRICE FOR CLINKER"

    The current lowest possible price based on FOB Bandar Abbass or BIK ports / Iran for different types of clinker is as the follows:

  15. White Clinker type I / Bulk without big bags : US$ 55.00 M/T

  16. White Clinker type I / Bulk in 1.5 M/T big bags : US$ 63.00 M/T

  17. Gray Clinker type I,II / Bulk without big bags : US$ 25.00 M/T

  18. Gray Clinker type I,II / Bulk in 1.5 M/T big bags : US$ 31.00 M/T

  19. Gray Clinker type V is US$ 4.00 M/T higher than the above gray clinker prices.

    20.  

    "PRICE FOR PORTLAND CEMENT"

  20. White Cement type I / Bulk without big bags : US$ 68.00 M/T

  21. White Cement type I / in 50 kg PP laminated bags : US$ 75.00 M/T

  22. White Cement type I / Bulk in 1.5 M/T big bags : US$ 75.00 M/T

  23. White Cement type I / 50 kg PP laminated bags in 1.5 M/T big bags : US$ 82.00 M/T

  24. White Cement type I / 50 kg PP laminated bags on 1.5 M/T Shrinked wooden pallet : US$ 84.00 M/T

  25. Gray Portland Cement type I and II / Bulk without big bags : US$ 29.00 M/T

  26. Gray Portland Cement type I and II / in 50 kg PP laminated bags : US$ 35.00 M/T

  27. Gray Portland Cement type I and II / Bulk in 1.5 M/T big bags : US$ 35.00 M/T

  28. Gray Portland Cement type I and II / 50 kg PP laminated bags in 1.5 M/T big bags : US$ 41.00 M/T

  29. Gray Portland Cement type I and II / 50 kg PP lam. bags on 1.5 M/T wooden pallet : US$ 42.00 M/T

PS: The price of OPC type V is US$ 4.00 M/T higher than OPC type I and II prices.

NOTE: All above prices is subject to change without notice and should re-confirm as per as any order.

ORDINARY PORTLAND CEMENT SPECIFICATIONS

(TYPE I, II & V)

(IN ACCORDANCE TO ASTM C150-97)

CHEMICAL COMPOSITION

Results %Wt.

Type I

Results %Wt.

Type II

Results %Wt.

Type V

SILICON DIOXIDE (Sio2)

20.80

20.0- 22.0

21.60

ALUMINUM OXIDE (Al203)

5.10

4.5 - 5.5

4.19

FERRIC OXIDE (Fe2O3)

3.21

3.5- 4.0

4.39

CALCIUM OXIDE (CaO)

64.30

62.0 - 66.0

63.60

MAGNESIUM OXIDE (MgO)

2.10

1.5 - 2.2

2.25

POTASSIUM OXIDE (K2O)

0.70

0.5 - 0.8

0.59

SODIUM OXIDE (Na2o)

0.39

0.3 - 0.6

0.22

SULFUR TRIOXIDE (SO3)

2.50

2.0 - 3.0

2.27

LIME SATURATION FACTOR (L.S.F)

96.92

92.0 - 97.0

43.15

CHOLORIDES

-

-

-

LOSS ON IGNITION (L.O.I.)

0.90

0.4 - 0.8

0.89

FREE LIME ( FREE CaO )

1.50

0.6 - 1.50

1.20

TRICALCIUM SILICATE (C3S)

57.70

40.0 - 60.0

53.86

DICALCIUM SILICATE (C2S)

16.16

15.0 - 30.0

21.36

TRICALCIUM ALUMINATE (C3A)

8.07

5.0 - 8.0

3.65

TRICALCIUM ALUMINO FERRICE (C4AF)

9.76

10.5 - 11.5

13.36

PHYSICAL PROPERTIES

Results

Results

Results

BLAIN cm2/gr.

2850

2800 - 3200

2900

AUTOCLAVE EXPANTION

0.05

0.01 - 0.20

0.07

INITIAL SETTIN TIME (VICAT) Minutes

135

140 - 180

140

FINAL SETTING TIME (VICAT) Minutes

165

270 - 300

180

COMPRESSIVE STRENGTH @ 03 DAYS kg/cm2

240

170 - 270

210

COMPRESSIVE STRENGTH @ 07 DAYS kg/cm2

320

270 - 350

300

COMPRESSIVE STRENGTH @ 28 DAYS kg/cm2

430

350 - 450

390

 

CLINKER SPECIFICATIONS

(TYPE I, II & V)

( IN ACCORDANCE TO ASTM C150-97 )

CHEMICAL COMPOSITION

Results % Wt.

Type I

Results % Wt.

Type II

Results % Wt.

Type V

SILICON DIOXIDE (Sio2)

21.87

20.0 - 22.0

21.90

ALUMINUM OXIDE (Al203)

5.29

4.50 - 5.50

4.20

FERRIC OXIDE (Fe2O3)

3.31

3.50 - 4.00

4.40

CALCIUM OXIDE (CaO)

65.90

62.0 - 67.0

65.55

MAGNESIUM OXIDE (MgO)

1.98

1.50 - 2.20

2.33

POTASSIUM OXIDE (K2O)

0.70

0.50 - 0.80

0.60

SODIUM OXIDE (Na2o)

0.41

0.30 - 0.60

0.22

SULFUR TRIOXIDE (SO3)

0.30

1.40 - 2.40

0.50

LIME SATURATION FACTOR (L.S.F)

94.64

90.0 - 100

94.81

SILICA MODULUS (SiM)

2.54

2.30 - 2.50

2.55

ALUMINUM MODULUS (AL.M)

1.60

1.30 - 1.50

0.95

LOSS ON IGNITION (L.O.I.)

0.24

0.01 - 0.80

0.30

INSOLUBLE RESIDUE (I.R.)

0.20

0.01 - 0.40

0.15

FREE LIME ( FREE CaO )

1.20

0.60 - 1.50

1.00

LITRIC WEIGHT (Lit/Kg)

1300

1200 - 1400

1300

PHASE COMPOSITION

Results

%Wt.

Results

%Wt.

Results

%Wt.

TRICALCIUM SILICATE (C3S)

61.80

40.0 - 60.0

65.91

DICALCIUM SILICATE (C2S)

16.15

15.0 - 30.0

13.13

TRICALCIUM ALUMINATE (C3A)

8.42

5.0 8.0

3.66

TRICALCIUM ALUMINO FERRICE (C4AF)

10.08

10.50 - 11.50

13.39

 

WHITE CLINKER SPECIFICATION TYPE ONE

IN ACCORDANCE TO ASTM C-150 97 B

CHEMICAL COMPOSITION

 

Test Result

Specifications

SILICON DIOXIDE

SIO2

23.5

-

ALUMINIUM TRIOXIDE

AL2o3

5.15

-

IRON TRIOXIDE

Fe2o3

0.34

-

CALCIUM OXIDE

Cao

06.7

-

MANGNESIUM OXIDE

Mgo

2

Max. 6.0%

SULPHUR TRIOXIDE

SO3

 

-

WHEN CSA IS 8% OR LESS

 

 

Max. 3.0%

WHEN CSA IS MORE THAN 8%

 

0.5

Max. 3.5%

SODIUM OXIDE

Na2o

0.1

-

POTASSIUM OXIDE

K2o

0.3

-

INSOLLBEL RESIDUE

%

0.2

Max. 0.75%

LOSS ON IGNITION

%

0.65

Max. 3.0%

UNDETERMINED

%

0.55

-

CALCULATED COMPONDS & OTHERS

 

 

 

L.S.F

 

92.51

-

TRICALCIUM SILICATE (C3S)

%

57.80

-

TRICALCIUM ALUMINATE (C3A)

%

13.07

-

EQUIVALENT ALKALIES (Na2o+0,658 k2O)

%

0.30

Max. 06

COLOR Y-VALUE

WHITENESS

%

83.1

92.1

 

 

WHITE CEMENT SPECIFICATION TYPE ONE

IN ACCORDANCE TO ASTM C-150 97 B

PHYSICAL REQUIERMENT

RESULTS

SPECIFICATION

FINENESS SPECIFIC SURFACE CM2/g

4100

Min 2800

SOUNDNESS AUTOCLAVE EXPASION %

0.15

Max 0.8

COMPRESSIVE STRENGTH PSI

 

 

3 DAYS PSI

3130

Min 1740

7 DAYS PSI

4140

Min 2760

28 DAYS PSI

5120

Min

INITIAL SETTING TIME MINS

140

Min 45

FINAL SETTING TIME MINS

260

Max 375

WHITENESS %

92.4

Min 92

CHEMICAL PROPERTIES

 

 

SILICON DIOXIDE ( SIO2 ) %

23.3

 

ALUMINIUM OXIDE ( AL2O3 ) %

4.8

 

IRON TRIOXIDE ( Fe2O3 ) %

0.43

 

CALCIUM OXIDE ( CaO ) %

65.5

 

MAGNESIUM OXIDE ( MgO ) %

1.35

Max 6

SULPHUR TRIOXIDE ( K2O ) %

1.8

Max 3.5 C3A>8%

 

 

Max 3.0 C#A<8%

SODIUM OXIDE ( Na2O ) %

0.34

 

POTASSIUM OXIDE ( K2O ) %

0.23

 

INSOLUBLE RESIDUE %

0.2

Max 0.75

LOSS ON IGNITION %

2.40

Max 3

UNDETERIMINED %

0.37

 

CALCULATED COMPONDS & OTHERS

 

 

TRICALCIUM SILICATE ( C3S ) %

51.50

 

TRICALCIUM ALUMINATE ( C3A ) %

11.99

 

EQUIVALENT ALKALIES ( Na2O - 0.658 K2O ) %

0.26

Max 0.6

 

In case you have any question, please feel free to contact us by Telefax: 0098-21-256 48 03 (Three Lines) or Email [email protected].

 

BACK TO HOME

 

Last update: July 2002

Hosted by www.Geocities.ws